- MakaleAçık Erişim2016Determining the Effect of Seasonal Variation in Spruce (Picea orientalis L.) Wood Treated with Various Impregnations on Combustion Resistance
Yasar, Ş. Şadiye; Fidan, M. Said; Yaşar, Mehmet; Atar, Musa; Alkan, Elif
Prepared test specimens were surface treated and coated with synthetic and water-based outdoor varnishes after being chemically impregnated. The test specimens were left outdoors to determine the effects of impregnation and treatment on the wood during each of the four seasons. Caucasian spruce (Picea orientalis L.) test specimens were prepared and combustion analyses were performed. As a result of the combustion test, weight loss results, as compared with the control, were 89% lower in the spring specimens, 90% lower with impregnation, and 90% lower with the synthetic varnish coating. Furthermore, the O2 amount during combustion was found to be the highest in combustion with a flame source in the winter specimens (21%). The CO2 amount was the highest in combustion without a flame source for full-year specimens (20%). The CO amount was the highest in combustion without a flame source of full-year specimens (31,787 ppm), and the NO amount was the highest during glowing of full-year specimens (55 ppm). Final results showed impregnation with Tanalith-E and water-based varnish coating to be the most effective fire protective treatments.
- MakaleYalnız künye2016Influences of seasonal alterations on the burning characteristics of impregnated and surface treated chestnut (Castanea sativa mill ) wood
Yasar, S. Sadiye; Fidan, Muhammed Said; Yasar, Mehmet; Atar, Musa; Alkan, Elif
Wood material is generally preferred due to its resilience against earthquakes, aesthetic properties, and its warmth as well as being natural. One of the major problems of employing this natural and breathable product is its ease of combustibility. Despite this adverse characteristic, its high resistance against burning and its ability to maintain its weight bearing characteristics until the very end does not lead to sudden collapses as is seen in steel and concrete systems. Treating wood with impregnating materials in order to improve its resistance against burning is an improved safety measure for the prevention of ignition. This study investigate seasonal effects on the ignition characteristics of chestnut wood samples impregnated using either Tanalith-E or Wolmanit-CB as detailed in ASTM-D 1413-76 and surface-treated using water-based or synthetic varnish as detailed in ASTM-D 3023- 88. The temperature of burning process was the highest in the investigated samples, in those impregnated with Wolmanit-CB and those that were treated with water-based varnish. The results of the study indicated that weight loss was lower during winter (84.59 %), for samples that were impregnated using Wolmanit-CB (84.46 %) and in those that were treated with water-based varnish (84.18 %). On the other hand, the O2 content was determined to be the highest and the CO content the lowest in winter samples that were impregnated using Wolmanit-CB and treated with synthetic varnish.