- MakaleYalnız künye2018Indication of the Screw Withdrawal Strength of Scots pine (Pinus sylvestris L.) Wood Impregnated with Quechua and Different Boron Compounds
Şen, Selim; Fidan, M. Said; Alkan, Elif; Yaşar, Ş. Şadiye
Wooden materials are conducted to prevent damages (biotic, abiotic pests, fire, etc.) from the environment and are used to extend the usage life of wooden materials. Due to this reason, this study is determined different screw withdrawal strength properties of wooden material impregnated with quechua, borax and boric acid. The scots pine (Pinus sylvestris L.) test specimens are prepared with borax, boric acid, borax + boric acid, from borax compounds which have a great potential in Turkey, and with quechua, one of the natural impregnation substances. Then these samples are impregnated with three different (1%, 3%, 5%) solution concentrations according to ASTM 1413-76 standards. After impregnation, screw withdrawal strength samples are determined compared with control samples. According to the test results; the highest screw withdrawal strength values are determined in solution concentrations with %5 concentration. The highest boron compound values are determined in solution concentrations with boric acid+borax compounds. In this case, the boric acid at a concentration of 1% can be preferred in solid wood applications such as in places which are not exposed to rain water.
- MakaleYalnız künye2018Determination of certain properties of scotch pine (Pinus sylvestris L.) wood which is impregnated with boron compounds and Quechua
Sen, Selim; Said Fidan, M.; Alkan, Elif; Sadiye Yaşar, S.
As the industrialisation and technological developments increase; the search for functional material which is environment-friendly, non-toxic, flame resistant, with a broad applicability and with high-temperature endurance also increases. Even though the wood material corresponds most of these features, its possession of an organic structure causes it to be affected negatively by damages occurring under proper conditions in the outdoor environment. Due to this reason, this study is conducted to prevent damages (biotic, abiotic pests, fire, etc.) caused by the environment to the wooden material, and to determine some physical and mechanical properties of wooden material impregnated with quechua, borax and boric acid, which are used to extend the usage life. Those features are needed in an outdoor environment. The Scotch pine (Pinus sylvestris L.) test specimens are prepared with borax, boric acid, borax+boric acid, from borax compounds, which have a great potential in Turkey, and with quechua, one of the natural impregnation substances. Then these samples are impregnated with three different (1%, 3%, 5%) solution concentrations according to ASTM 1413-76 standards and some physical-mechanical property changes are investigated. After impregnation, samples are tested and compared with control samples. According to the test results; the lowest oven dried density change is obtained in borax as 0.46 g . cm -3 in terms of boron compounds and the retention amount is determined to be highest with 3.83 kg.m -3 in the samples impregnated with boric acid. The bending strength and elastic modulus are found to be highest with 83.53 MPa and 10281 MPa in the samples impregnated with boric acid. When examined at the concentration level, it is determined to be highest with 81.89 MPa in samples with 3% concentration. There are statistical discrepancies with 55.77 MPa in the comprehensive strength parallel to grain in boric acid in terms of boron compounds.
- MakaleYalnız künye2017Combustion properties of impregnated spruce (Picea orientalis L.) wood
Şadiye Yasar, Ş.; Said Fidan, M.; Yaşar, Mehmet; Atar, Musa; Alkan, Elif
Wooden material is one of the most commonly used construction materials since history of humanity due to its environment friendly and renewable natural source. This structure of wood material is also preferred because it is lightweight, easy to work, resistant to factors such as earthquake and fire, as compared to other used building materials. However, organic structure of the wooden material causes it to be affected negatively because of damages that might occur outdoors under inappropriate conditions. Due to this reason, in this study were investigated effects of various chemicals (impregnated and varnish type), used to prevent environmental damages (biotic, abiotic pests, fire etc.) on combustion resistance of the wood exposed to air conditions for a year. For this purpose, prepared Caucasian spruce (Picea orientalis L.) specimens were surface treated (synthetic and water-based varnish) after impregnated according to ASTM-D 1413-76 principles with various chemicals (Tanalith-E and Wolmanit-CB). Test specimens with impregnated, varnished and processless, were left in outdoor conditions for a year. Combustion experiment was conducted according to the principles in ASTM-E 160-50 combustion test standards. According to the results of the experiment, control and year specimens had close results in the weight loss. Weight loss was found be lower Wolmanit-CB impregnated specimens (92.12%) among the impregnated materials to synthetic varnish coated specimens (% 91.89) among the varnished specimens. It was determined that using Wolmanit-CB for impregnating and synthetic varnish for varnishing would be better according to the results. Furthermore, the amount of O2 (25.84 ppm) in control specimens in combustion with flame; the amounts of CO and CO2 (31787, 19.92 ppm respectively) in year specimens in combustion without flame and the amount of NO (54.65 ppm) in year specimens in glowing was observed to be the highest.
- MakaleYalnız künye2016Saunaların Yapım Teknikleri ve Tek Kişilik Konut Tipi Sauna Örneği
Fidan, M. Said; Kale, Brış; Yaşar, Memet; Yaşar, Şadiye Ş; Alkan, Elif; Altinok, Mustafa
Doğada, sıcak ve soğuk olmak üzere birbirine zıt iki kutup vardır. Sauna bu tezatların bir uygulama mekanıdır. Sauna, hava ve su vasıtasıyla soğutulan bir sıcak hava banyosudur. Bu banyo ile insan bedeni, soğuk ile sıcak arasındaki doğanın mücadelesini küçük çapta da olsa uygulamasını yaşamaktadır. Buna göre; sauna, sıcak ile soğuğun etkileri arasındaki sonsuz çekişmeyi temsil etmektedir. Sauna, bu iki büyük tesiri ideal bir şekilde bünyesinde toplamaktadır. Bu çalışmada, saunaların yapım teknikleri hakkında literatür taramaları ve tek kişilik konut tipi sauna yapımı örneklendirilmiştir. Çalışma sonunda; elde edilen teknik dokümanlar ve edinilen tecrübeler ile bütün tasarlanmış saunalara yeni bir alternatif olarak, konut tipi mekanlar için banyoda tek kişilik bir sauna modeli geliştirilmeye çalışılmıştır
- Derleme MakaleYalnız künye2016Characterization of the Combustion Parameters of Impregnated and Varnished Cedar Wood (Cedrus libani)
Fidan, M. Said; Yasar, S. Sadiye; Yasar, Mehmet; Atar, Musa; Alkan, Elif
The present study investigated the effect of various types of impregnating and surface treatment materials on the fire resistance of wood material indoors and outdoors. Wood samples (Cedrus libani A. Rich.) were impregnated with Wolmanit-CB or Tanalith-E according to ASTM D1413-76 (American Society for Testing and Materials 1976). The impregnated surface was treated with either synthetic or water-based outdoor varnish materials. The impregnated and varnished samples were left in outdoor conditions for 1 year. The combustion characteristics of the samples were investigated at the end of 1 year according to the combustion parameters detailed in the ASTM E160-50 (1975) combustion test. The results of this study indicated that the combustion parameters were lower in the 1-year-old samples (89.12% of control values), in the samples impregnated using Wolmanit-CB (89.18% of control values), and in samples treated using water-based varnish (88.43% of control values). The analysis of flue gas indicated that the O-2 content of the 1-year-old samples impregnated with Wolmanit-CB and treated with synthetic varnish was higher, whereas the CO content was lower. In conclusion, impregnated Wolmanit-CB specimens provide higher fire resistance.
- MakaleAçık Erişim2016Combustion Characteristics of Impregnated and Surface-treated Chestnut (Castanea sativa Mill.) Wood Left Outdoors for One Year
Fidan, Muhammed Said; Yaşar, Şekip Şadiye; Yaşar, Mehmet; Atar, Musa; Alkan, Elif
Treating wood with impregnating materials in order to improve resistance to burning is a commonly employed safety measure. In this study, chestnut (Castanea sativa Mill.) wood samples were impregnated using either Tanalith-E or Wolmanit-CB according to ASTM-D 1413-76 and surface-treated using water-based or synthetic varnish according to ASTM-D 3023. These samples were used to investigate the combustion characteristics of samples left outdoors for one year as detailed in ASTM-E 160-50. The combustion temperatures of the samples left outdoors were similar upon impregnation with either Tanalith-E or Wolmanit-CB. However, the combustion temperature of the samples treated with synthetic varnish was lower than those that were treated with water-based varnish. The time to collapse and the total duration of combustion of the samples left outdoors were shorter for those impregnated with Wolmanit-CB. Weight loss of the samples left outdoors was higher for those that were impregnated with Tanalith-E and treated with water-based varnish. Gas analysis of the samples that were left outdoors indicated that the O2 content of flue gas from samples that were impregnated with Wolmanit-CB and treated with synthetic varnish was high and the CO content of flue gas from the same samples was low.
- MakaleAçık Erişim2016Determining the Effect of Seasonal Variation in Spruce (Picea orientalis L.) Wood Treated with Various Impregnations on Combustion Resistance
Yasar, Ş. Şadiye; Fidan, M. Said; Yaşar, Mehmet; Atar, Musa; Alkan, Elif
Prepared test specimens were surface treated and coated with synthetic and water-based outdoor varnishes after being chemically impregnated. The test specimens were left outdoors to determine the effects of impregnation and treatment on the wood during each of the four seasons. Caucasian spruce (Picea orientalis L.) test specimens were prepared and combustion analyses were performed. As a result of the combustion test, weight loss results, as compared with the control, were 89% lower in the spring specimens, 90% lower with impregnation, and 90% lower with the synthetic varnish coating. Furthermore, the O2 amount during combustion was found to be the highest in combustion with a flame source in the winter specimens (21%). The CO2 amount was the highest in combustion without a flame source for full-year specimens (20%). The CO amount was the highest in combustion without a flame source of full-year specimens (31,787 ppm), and the NO amount was the highest during glowing of full-year specimens (55 ppm). Final results showed impregnation with Tanalith-E and water-based varnish coating to be the most effective fire protective treatments.
- MakaleYalnız künye2016Influences of seasonal alterations on the burning characteristics of impregnated and surface treated chestnut (Castanea sativa mill ) wood
Yasar, S. Sadiye; Fidan, Muhammed Said; Yasar, Mehmet; Atar, Musa; Alkan, Elif
Wood material is generally preferred due to its resilience against earthquakes, aesthetic properties, and its warmth as well as being natural. One of the major problems of employing this natural and breathable product is its ease of combustibility. Despite this adverse characteristic, its high resistance against burning and its ability to maintain its weight bearing characteristics until the very end does not lead to sudden collapses as is seen in steel and concrete systems. Treating wood with impregnating materials in order to improve its resistance against burning is an improved safety measure for the prevention of ignition. This study investigate seasonal effects on the ignition characteristics of chestnut wood samples impregnated using either Tanalith-E or Wolmanit-CB as detailed in ASTM-D 1413-76 and surface-treated using water-based or synthetic varnish as detailed in ASTM-D 3023- 88. The temperature of burning process was the highest in the investigated samples, in those impregnated with Wolmanit-CB and those that were treated with water-based varnish. The results of the study indicated that weight loss was lower during winter (84.59 %), for samples that were impregnated using Wolmanit-CB (84.46 %) and in those that were treated with water-based varnish (84.18 %). On the other hand, the O2 content was determined to be the highest and the CO content the lowest in winter samples that were impregnated using Wolmanit-CB and treated with synthetic varnish.
- MakaleYalnız künye2016Effect of seasonal changes on the combustion characteristics of impregnated cedar (Cedrus libani A. Rich.) wood
Fidan, M. Said; Yaşar, Ş. Şadiye; Yaşar, Mehmet; Atar, Musa; Alkan, Elif
Wood is an irreplaceable material used as decorative and structural element both indoors and outdoors. When used as a structural material, wood has several superior characteristics in comparison to other structural constituents, although it is adversely affected by fires as well as biotic pests and abiotic effects. In this study, cedar (Cedrus libani A. Rich.) wood samples were impregnated using either Tanalith-E or Wolmanit-CB as detailed in ASTM-D 1413-76 and surface-treated using water-based or synthetic varnish. The impregnated and varnished samples were left outdoors with the aim of investigating the effect of seasonal changes. The samples were later subjected to combustion analysis as detailed in the combustion test standard ASTM-E 160-50. The results of the study indicated that the weight loss was lower during winter (87.82%), for samples that were impregnated using Wolmanit-CB (88.90%) and those that were treated with synthetic varnish (88.45%). On the other hand the O2 and CO2 contents were determined to be the highest in fall during combustion without flame (18.16% and 17.96%, respectively); the CO content was the highest during combustion without flame for the winter samples (28,907 ppm) and the NO content was the highest during combustion without flame for the spring samples (76.15 ppm). In conclusion, the winter samples that were impregnated using Wolmanit-CB and treated with synthetic varnish were determined to be safer to employ in areas with high fire risk.