  Investigation of the adhesion properties of duplex coating on AZ91 alloy surface by MAO/HiPIMS-PVD methods

  Kaplan, Emine Boynueğri; Şüküroğlu, Süleyman; Şüküroğlu, Ebru Emine

  This study focuses on enhancing the surface properties and minimizing the mechanical incompatibility between the AZ91 magnesium alloy and the coating by applying CrAlYN/CrYN gradient coatings through the HiPIMS-PVD method, combined with the enlargement of a MgO intermediate layer via the Micro Arc Oxidation (MAO) method. The duplex coating approach was designed to strengthen adhesion and structural integrity between the substrate and the coating. Coating parameters for both MAO and HiPIMS-PVD processes were optimized using a Taguchi L4 orthogonal array, and the coatings were analyzed using SEM, EDS, XRD and scratch testing. MAO coatings exhibited porous and rough surfaces with volcanic morphologies. The best adhesion performance under MAO conditions was achieved with 650 V, 700 Hz, and a Type B solution, resulting in a critical load value of Lc₂ = 24 N. CrAlYN/CrYN gradient coatings alone showed coating thicknesses from 0.83 μm to 1.66 μm with compact and homogeneous microstructures. Adhesive strength was relatively low (Lc₂ = 5–10 N). In the duplex coating configuration, CrAlYN/CrYN coatings were deposited on the MAO-formed MgO layer, significantly increasing adhesion. Critical load values (Lc₂) ranged from 90 to 110 N, with the highest adhesion achieved under low CrY target voltage and current conditions. The findings demonstrate that the MAO/HiPIMS-PVD duplex coating method substantially improves adhesion and surface characteristics of AZ91 alloy, offering a promising solution for advanced surface engineering applications.

  İncele
• MakaleYalnız künye2025/r/gumushane/14079
  Investigation of structural and adhesion properties of ZnO and h-BN doped TiO2 coatings on Cp–Ti alloy

  Belet, Ali Kadir; Şüküroğlu, Süleyman; Şüküroğlu, Ebru Emine

  Titanium and its alloys are widely used in aircraft, automotive, chemistry, marine, and military industries owing to their superior properties such as specific strength, very low density, high melting point, high corrosion resistance, good fatigue strength and toughness, low elastic modules, and excellent biocompatibility. However, insufficient tribological properties such as high and unstable friction coefficient, low scraping wear resistance and strong adhesion tendency, and poor corrosion resistance in some aggressive corrosive environments such as severe chloride solution limits the use of titanium and its alloys in some engineering applications. For this reason, it has become quite common to change and/or improve the surface properties of titanium and its alloys. In this study, the structural properties of TiO2 coatings with zinc oxide (ZnO) added TiO2 and hexagonal boron nitride (h-BN) added TiO2 grown composite coatings, respectively, on Cp–Ti substrates by micro-arc oxidation method and the adhesion behavior between the base material and coatings were investigated.

  İncele
• MakaleAçık Erişim2025/r/gumushane/13991
  Effect of sodium pentaborate (B5H10NaO13) nanoparticle addition to oxide coatings grown on AZ31 magnesium alloy by micro arc oxidation method on mechanical, corrosion and adhesion properties of coatings; [Efecto de la adición de nanopartículas de pentaborato de sodio (B5H10NaO13) en los recubrimientos de óxido formados sobre la aleación de magnesio AZ31 mediante el método de Microoxidación por Arco, sobre las propiedades mecánicas, de corrosión y de adhesión de los recubrimientos]

  Sukuroglu, Suleyman

  AZ31 magnesium alloy is one of the lightweight metallic engineering materials that are widely used in many industrial areas such as aviation, space, automobile and electronics industries, biomedical applications, where structural weight reduction is at the forefront of design principles. This study focuses on the growth of MgO and MgO:B5H10NaO13 doped oxide coatings on the surface of AZ31 magnesium alloy by micro arc oxidation (MAO) method in order to improve its usage areas and lifetime in industrial applications, and to investigate the structural, morphological, adhesion and corrosion properties of the grown coatings. In the study, MgO coatings were grown by MAO method and MgO:B5H10NaO13 doped composite oxide coatings were grown by adding sodium pentaborate (B5H10NaO13) nanoparticles into the electrolytic solution in MAO method. The phase structure of the grown coatings was determined by X-ray Diffraction (XRD), microstructure by Scanning Electron Microscopy (SEM) and chemical composition by Energy Dispersive X-ray Spectroscopy (EDS). The hardness of MgO and MgO:B5H10NaO13 doped composite oxide coatings were determined by microhardness tester, the adhesion resistance with the base material was determined by Scratch Tester and the corrosion resistance was determined by potentiodynamic polarization tester. As a result, it was observed that dense and homogeneous coatings were grown on the surfaces of particle-added (MgO:B5H10NaO13) coatings, that porosity and pore sizes on the surfaces of the coatings were reduced, that microcracks were reduced, and that coatings with high bond strength with the base material were grown. It was also determined that the corrosion resistance of the coatings with particle addition (MgO:B5H10NaO13) was higher than the corrosion resistance of the coatings without particle addition (MgO).

  İncele
• MakaleYalnız künye2025/r/gumushane/12355
  Characterization, corrosion, adhesion and wear properties of Al2O3 and Al2O3:TiB2 composite coating on Al 7075 aluminum alloy by one-step micro-arc oxidation method

  Sukuroglu, Suleyman

  This study was carried out in order to increase the usage areas of Al 7075 alloy, which is preferred as an engineering material in the aerospace industry, defense industry and automotive industry, in high temperature applications, wear resistance in different environments and corrosion resistance in aggressive environments. For this purpose, the focus was on the growth of Al2O3 and Al2O3:TiB2 doped composite coatings on the surface of Al 7075 aluminum alloy by the MAO method, and the structural, morphological, corrosion, adhesion and wear properties of the grown coatings in three different environments (atmospheric conditions, brine containing 3.5 % NaCl and oil). Firstly, Al2O3 coatings were grown in electrolytic solution number 1. Secandly, Al2O3:TiB2 doped composite coatings were grown in electrolytic solution number 2 and the phase structure, microstructure and chemical composition of the grown coatings were determined by X-ray Diffraction, Scanning Electron Microscopy, Energy Dispersive X-ray Spectroscopy, respectively. The abrasion behavior of the coatings in three different environments was determined by a pin-on disc abrasion tester, adhesion resistances were determined by a Scratch Test, and corrosion resistance was determined by a potentiodynamic polarization tester. It was observed that dense and uniform coatings were grown on the surfaces of TiB2 nanoparticle-added (Al2O3:TiB2) coatings, porosity and pore sizes on the surfaces of the coatings were reduced and microcracks were reduced. In addition, it was determined that the corrosion resistance and wear resistance of composite coatings (Al2O3:TiB2) grown with nanoparticle addition increased, and coatings with high bond strength with the substrate were grown.

  İncele
• MakaleYalnız künye2024/r/gumushane/16054
  Investigation of Corrosion Properties of LA-91 Alloy Coated with MAO Method

  Sukuroglu, Suleyman; Totik, Yasar; Sukuroglu, Ebru Emine; Avci, Selcuk

  LA91 magnesium alloy is a super lightweight magnesium -lithium alloy proposed for next generation materials. In addition to the advantages of these alloys such as low density, high strength-to -weight ratio, specific stiffness and brittleness, these alloys also have disadvantages such as low corrosion resistance and the oxide -carbonate film formed on the surfaces of the alloys cannot provide sufficient corrosion protection even in non-corrosive environments. In this study, micro arc oxidation, one of the coating methods, was applied to LA91 alloy. The surface morphologies of the coatings were characterized and it was aimed to increase the corrosion resistance of LA91 alloy. For this purpose, potentiodynamic polarization tests were carried out in 3.5% NaCl solution at room temperature to draw attention to the protection of the coating. As a result of the tests, it was determined that the oxide coatings raised on the surface

  İncele
• MakaleAçık Erişim2024/r/gumushane/11661
  Corrosion and adhesion properties of MAO-coated LA91 magnesium alloy

  Sukuroglu, Suleyman; Sukuroglu, Ebru Emine; Totik, Yasar; Gulten, Gokhan; Efeoglu, Ihsan; Avci, Selcuk

  Magnesium–lithium alloy is used in different areas of industry and is known as a super light metallic engineering material. However, the use of these alloys is limited due to their surface properties under extreme loads and aggressive environments. Surface treatments can be applied to these alloys to increase their usage areas and improve their weak surface properties. In this study, the micro-arc oxidation method was applied to improve the surface properties of LA91 alloy. The corrosion and adhesion behaviour of the coated samples were investigated. The lowest corrosion current density in the coatings was obtained under Experiment 3. Experiment 3 has the highest Lc2 value due to the coating thickness and the denser and smaller diameter pores of the functional intermediate layer.

  İncele
• MakaleAçık Erişim2023/r/gumushane/20273
  Al 2024 Alaşımı Üzerine Mikro Ark Oksidasyon Yöntemiyle B4C İlaveli Kompozit Kaplamaların Büyütülmesi

  Sukuroglu, Suleyman

  Al alaşımı üzerinde Mikro ark Oksidasyon (MAO) yöntemiyle büyütülen kaplamaların yapısı ve özellikleri üzerine Bor karbür (B4C) katılmasının etkisi, sodyum fosfat, sodyum silikat ve potasyum hidroksitten oluşan bir çözelti içerisinde gerçekleştirilerek araştırılmıştır. MAO, B4C parçacıkları eklenmiş ve eklenmemiş çözeltilerde Al 2024 alaşımı üzerine uygulanmıştır. MAO kaplamalarının faz bileşimi ve mikro yapısı X-ışını kırınımı difraktometresi (XRD) ve taramalı elektron mikroskobu (SEM) kullanılarak değerlendirilmiştir. Ayrıca kaplamaların, mikrosertlik değerleri mikrosertlik test cihazı kullanılarak tespit edilmiştir. Al alaşımı üzerindeki oksit kaplamaların birincil olarak γ- Al2O3'ten oluştuğu gözlenmiştir. Solüsyona ilave edilen B4C partiküllerinin eklenmesi, MAO kaplamalarının Al alaşımları üzerindeki oluşum hızını ve kompaktlığını iyileştirdiği ve X-ışını kırınımı yoluyla kaplamalarda B4C varlığı tespit edilmiştir. Yüksek sertlik ve iyi kimyasal stabiliteye sahip B4C parçacıkları, MAO kaplamalarında eşit olarak dağıldığı gözlenmiştir. Bu nedenle, B4C takviyeli MAO kaplamaların sertlik değeri, Al alaşımları üzerindeki B4C ilave edilmeyen oksit kaplamalardan belirgin şekilde yüksek olduğu gözlenmiştir.

  İncele
• MakaleAçık Erişim2023/r/gumushane/20208
  Radyasyona Maruz Kalan Sağlık Personellerinin Tükenmişlik Düzeylerinin Belirlenmesi

  Sukuroglu, Ebru Emine; Sukuroglu, Suleyman; Günaydın, Mustafa; Demir, Hatice

  Kaliteli sağlık bakımı elde edebilmek için, sağlık çalışanlarının çalışma alanlarında sağlıklı ve güvenli çalışma koşulları oluşturulmalıdır. Bunun sağlanabilmesi için çalışanın fiziksel, sosyal ve ruhsal olarak iyi olmasının yanı sıra kendilerini güçlü hissetmeleri de gerekmektedir. Çalışma ortamında stres ve psikososyal riskler ise tükenmişliğe neden olmaktadır. Tükenmişlik ise sağlık personellerinde sıklıkla karşılaşılan, çalışanların performansına olumsuz etki eden önemli bir durumdur. Bu çalışmada iyonlaştırıcı radyasyon kaynakları ile çalışan sağlık personellerinin tükenmişlik durumlarının belirlenmesi amaçlanmıştır. Çalışmada hastanelerin çeşitli birimlerinde çalışan 154 sağlık çalışanı üzerinde demografik özelliklerden (25 adet) ve Maslach tükenmişlik envanterinden (22 adet) oluşan 47 soruluk anket uygulanmıştır. Maslach tükenmişlik envanteri, duygusallık yönünden tükenmişlik, kişisel başarı ve duyarsızlaşma şeklinde üç alt boyuttan oluşmaktadır. Anketin güvenirlilik analizi değeri Cronbach Alpha (α) ile hesaplanmış ve 0,84 olarak bulunmuştur. Çalışmanın sonucunda demografik özellikler ile tükenmişlik ölçeği arasında anlamlı farklılıklar ortaya çıkmıştır. Cinsiyet durumuna göre çalışanların duygusal tükenme, duyarsızlaşma ve kişisel başarı alt boyutlarında anlamlı fark olduğu tespit edilmiştir. Özellikle kadın çalışanların daha fazla tükenmişlik yaşadığı, yaş düzeyinin artmasının tükenmişlik ile ters orantılı olduğu belirlenmiştir. Bunun yanında sağlık çalışanlarının eğitim durumları ile tükenmişlik ölçeği arasında da anlamlı farklılıklar olduğu belirlenmiştir. Özellikle hemşirelerin hekimlere göre daha fazla duygusal tükenme yaşadığı görülmüştür.

  • 
  • 
  İncele
• MakaleYalnız künye2023/r/gumushane/14524
  The Effect of Surface Roughness on Fatigue Life in AZ31 Magnesium Alloy

  Karabudak, Filiz; Şüküroğlu, Ebru Emine; Şüküroğlu, Süleyman; Yeşildal, Ruhi

  Magnesium alloys have excellent properties such as high specific strength, rigidity, good damping, electromagnetic shielding, castability, and machinability. However, corrosion, creep, and fatigue resistance are generally the properties that need to be improved. In this study, a hybrid coating was formed on AZ31 magnesium alloy with different surface roughness at different frequencies. In the hybrid coating, an oxide coating was first grown on the surface by the micro-arc oxidation method, and then, the epoxy coating was grown on this oxide coating by the dipping method. The characterization of the coatings was performed by XRD, SEM, and EDS analysis. Furthermore, the relationship between fatigue life and surface roughness was also discussed in this study. The fatigue life and strength of the coated samples were determined as a result of the tests performed on the fatigue device. It was concluded that the fatigue life and strength of hybrid coatings were much better compared to uncoated and single-layer coated samples.

  İncele
• MakaleAçık Erişim2022/r/gumushane/17133
  İş Sağlığı ve Güvenliği ve İş Verimliliği Etkileşimi: Açık Ocak Maden İşletmesi

  Sukuroglu, Ebru Emine; Sukuroglu, Suleyman; Günaydın, Mustafa; Bayrak, Ayşe

  Bu çalışmada, açık ocak maden faaliyeti yürüten bir maden firması çalışanlarının iş sağlığı ve güvenliği ve iş verimliliği arasındaki ilişkiyi incelemiştir. Maden firmasına ait saha içerisinde önceden yaşanan kazalar ve alınan önlemler incelenmiştir. Demografik özellikler, iş sağlığı ve güvenliği ve verimlilik durumları ile ilgili anket formları düzenlenmiştir. İlgili formlar 56 kişiye uygulanmış ve tamamı değerlendirmeye alınmıştır. İşyerlerinde çalışan güvenliğini tehdit eden risklerin olması çalışanların verimliliğini önemli ölçüde olumsuz etkilediğini bulduk. Sağlık ve güvenlik önlemlerinin alınması ise çalışanların özgüvenlerini arttırdığı gibi işe karşı olan aidiyet duygularını da olumlu etkilemiştir. Çalışmamızda eğitim durumları ortaöğretim ve altında olanların iş kazası yaşaması (%10,7) daha fazla iken eğitim seviyesi yüksek olanların daha az (%1,7) olduğu bulunmuştur. Mesleki deneyim durumları incelendiğinde ise 5-10 yıl çalışanlar daha fazla iş kazasına (%5,3) maruz kalmıştır. Bu durum gereksiz özgüven, çalışırken gerekli ve dikkati göstermemelerinden kaynaklandığını söyleyebiliriz. İşyerlerinin iş güvenliği konusunda yapmış oldukları proaktif uygulamalar çalışanların verimliliğini arttırmıştır. Aynı şekilde yaşanan bir iş kazasından sonra alınan reaktif önlemler çalışanların daha dikkatli olmasına neden olmuştur. Çalışmamız işe bağlılığın daha yüksek yaş, daha düşük eğitim ve çevresel risk (düşük ve yüksek) ile önemli ölçüde ilişkili olduğunu göstermektedir.

  • 
  • 
  İncele