- MakaleAçık Erişim2025Scopus SJRQ4Long-term mechanical and physical behavior of rural concrete roads: A case study from Trabzon; [Kırsal beton yolların uzun vadeli mekanik ve fiziksel davranışı: Trabzon’dan bir vaka çalışması]
Seferoğlu, Mehmet Tevfik; Lermioğlu, Fatma
This study evaluates the long-term mechanical and physical performance of rural concrete pavements-defined as two-lane, unreinforced jointed plain concrete pavements constructed with a C25 mix design, an average slab thickness of 18–20 cm, serving low-to-moderate traffic volumes (<500 vehicles/day, <10% heavy vehicles), and built directly over compacted granular subgrade-using cylindrical core samples extracted from five neighborhoods in Trabzon, Türkiye: Çal, Gökçeler, Derecik, Çiğdemli, and Yolgören. Laboratory tests included compressive strength, splitting tensile strength, elastic modulus, capillary water absorption, and abrasion resistance. Yolgören exhibited the most severe deterioration, with a 34.84% loss in compressive strength, the lowest tensile strength, and the highest abrasion loss (0.088%), primarily attributed to poor drainage and heavy traffic. Derecik showed 22.18% strength loss and the lowest elastic modulus (14.9×103 MPa), likely due to weak subgrade and freeze-thaw cycles. Çal displayed moderate strength but had the highest capillarity coefficient and significant stiffness reduction (elastic modulus: 15.7×103 MPa), indicating high porosity and freeze-thaw damage. Çiğdemli performed best in surface durability, with the lowest abrasion loss (0.026%) and satisfactory elastic modulus. Gökçeler presented a rare case of strength gain (+0.85%) and retained acceptable stiffness, though minor surface wear (abrasion loss: 0.038%) was observed. These findings demonstrate that mix design alone does not guarantee long-term durability in rural pavements. Site-specific factors-such as curing effectiveness, drainage planning, subgrade preparation, and climate-must be considered in pavement design. A context-sensitive, performance-based approach is recommended for the sustainable development of rural road infrastructure.
- MakaleAçık Erişim2021Scopus SJRQ4Evaluation of Load-Transfer Efficiency of Steel Mesh Reinforced Contraction Joints in Concrete Pavement: Accelerated Pavement Test and FE Analysis
Celik, Muhammet; Seferoglu, Mehmet Tevfik; Akpinar, Muhammet Vefa; Nasery, Mohammad Manzoor; Seferoglu, Aysegul Gunes
Transverse contraction joints are by far the most common type of joint in jointed plain concrete pavements. Early loading of contraction joints can create a weakened vertical plane and later grow as a full-depth crack. In this study, load transfer efficiency (LTE) of steel mesh reinforced transverse contraction joints were studied at accelerated pavement tests (APT). 3D finite element (FE) model of jointed plain concrete pavement (JPCP) was developed to study deflections and crack propagation in just under the joint of the concrete pavement. The APT tests were focused on the LTE values before and after the crack initiation under the contraction joint region. Experiments were performed on three slabs in which two of these slabs were prepared without reinforcement and one of them was reinforced with steel mesh. Data generated by APT was used for verification of crack propagation modeling in the finite element analysis. Steel mesh reinforced slab gave the lowest vertical deflections (51μm) and highest LTE (91.56%). The LTE value in the reinforced slab after 25,000 passes was 13.63% higher than the average of unreinforced slabs. The findings suggest that the load transfer efficiency was found to be a complex parameter and should be interpreted together with average displacement values when contraction joints are evaluated at early traffic loadings.
AtıfScopus3WoS2OpenAlex2TR Dizin1
İncele - MakaleAçık Erişim2017Scopus SJRQ3Effects of fine aggregate abrasion resistance and its fineness module on wear resistance of Portland cement concrete pavements
Karpuz, Orhan; Akpinar, Muhammet Vefa; Aydin, Metin Mutlu
In this research, effects of fine aggregate abrasion resistance and its fineness module on wear resistance of Portland cement concrete pavements studied. Concrete samples included fine crushed limestone aggregate, fine crushed limestone-basalt mixture, and fine crushed basalt aggregate. The study results showed that LA abrasion rate of 30 % or less of fine aggregates would be necessary for long lasting concrete roads. Furthermore, it was found that fine aggregate's fineness module of 3.15 will significantly increase concrete road surface's wear resistance. As the fine aggregate's fineness module value increased from 2.2 to 3.15, the concrete's wear amount decreased to 15.5 %. Study findings also showed that using basalt aggregates instead of widely used limestone aggregates, will significantly increase pavement concrete wear resistance.
AtıfScopus8WoS4OpenAlex6İncele