- MakaleYalnız künye2020Comparative Investigation on Magnetic Behavior of Partial Rare Earth Element (Re: Lu, Yb, and Dy) Substituted Y0.5Re0.5BCO (123) Superconductors
Öztürk, Ali; Düzgün, İbrahim; Başoğlu, Mehmet; Çelebi, Selahattin
Partial Re (rare earth elements: Lu, Yb and Dy) substituted YBaCuO (123) superconductors synthesized by solid-state reaction (SSR) procedure have been investigated via x-ray diffraction, scanning electron microscopy, a.c. magnetic susceptibility, and d.c. magnetization, and calculations. The measurements of a.c. magnetic susceptibility have been carried out at constant a.c. field amplitude and constant frequency for the samples studied. The temperature dependence of intergranular critical current density (Jcm) has been estimated from the a.c. magnetic susceptibility data. The d.c. magnetization measurements were performed at the temperatures of 5 K, 20 K, and 77 K separately. The variation of critical current density (Jc) with magnetic field (μ0H) has been evaluated from the d.c. magnetization data by using upper and lower branch of the major hysteresis curve. Lu substituted Y0.5Lu0.5BCO (123) sample shows higher critical current density than Yb and Dy substituted samples at low-temperature (lower than 77 K) regions.
- MakaleYalnız künye2016The Effect of Dy Doping on the Magnetic Behavior of YBCO Superconductors
Öztürk, Ali; Doğan, Mustafa; Düzgün, İbrahim; Çelebi, Selahattin
The effect of dysprosium (Dy) doping on yttrium barium copper oxide (YBCO) prepared by conventional solid-state reaction method has been investigated by means of XRD, AC susceptibility, and DC magnetization measurements. AC susceptibility measurements for sintered YBCO pellets have been performed as a function of temperatures at constant frequency and AC field amplitude in the absence of a DC bias field. DC magnetization measurements were done at 5, 20, and 77 K upon zero field cooling (ZFC) process. The magnetization measurements showed a paramagnetic behavior existing at high magnetic fields. The magnetic field dependence of critical current density of the samples has been estimated from DC magnetization data. The partial Dy substitution for Y on YBCO superconductors improves the bulk critical current density at high magnetic fields and at high-temperature regions (higher than 20 K).