- MakaleYalnız künye2021Scopus SJRQ3The First Measurement for Mass Attenuation Coefficients, Effective Atomic Numbers, and Electron Densities of Y123 and Y358 High-Temperature Superconductors (HTS) for the Energies from 46.6 to 1332 keV
Düzgün, İbrahim
Y123 and Y358 high-temperature superconductor phases have experimental mass attenuation coefficients (MAC) determined at 46.5, 81, 122, 302, 356, 383, 662, 1173, and 1332 keV photon energies. The experimental values have been compared with theoretical values acquired employing the XCOM software and database. It has been observed that the theoretical and the empirical results were in perfect agreement. Also, it has been seen that the comparison of the MACs for all specimens examined with the corresponding photon energies complies with the exponential absorption law. The effective atomic numbers (Zeff) and electron densities (Nel) of Y123 and Y358 superconducting phases in different energy ranges have determined experimentally and theoretically. The Y358 superconductor specimen is a relatively better absorber than the Y123 between 40 and 100 keV.
AtıfScopus3WoS4OpenAlex2
İncele - MakaleYalnız künye2021Scopus SJRQ3Specification of Some Superconductivity Parameters by Adding Lutetium to the YBCO (358) Ceramic Superconductor
Başoğlu, M.; Düzgün, I.; Öztürk, A.
Superconducting specimens of Y3-xLuxBa5Cu8O18+δ (where x = 0, 0.2, 0.4, 0.5) ceramic were fabricated via the solid-state route (SSR). The structural and superconducting features of the specimens were analyzed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Measurements and calculations were carried out for electrical resistance (R-T) and DC magnetization (M-H). The onset critical transition temperature (Tconset) of the specimens dropped to lower temperatures with the addition of lutetium (Lu). The estimated critical current density (Jc) values of the specimens, depending on the magnetic field, were extracted from the DC magnetization data. The changes in average grain size and bulk critical current density were examined. Improvement was observed in the bulk critical current density with increasing levels of Lu/Y substitution.
AtıfScopus10WoS10OpenAlex10İncele - MakaleAçık Erişim2018Scopus SJRQ4The investigation of the lattice strains and crystallite sizes of Y358 and Y123 high-temperature superconductors
Duzgun, Ibrahim
In this study, the Y358 phase, the newest high-temperature superconductor member of the yttrium barium copper oxide family, was produced using the solid-state reaction technique. The Y358 superconductor exhibited the Meissner effect at low temperature (77 K). The X-ray diffraction spectra indicated that the crystal structure was almost identical to that of Y123, but with some impurity peaks. An X-ray peak broadening analysis was applied to determine the lattice strain, and the medial crystallite size was calculated perpendicular to the surface of the superconductor specimens. As a result of the analyses, it was determined that the crystallite size of the Y358 superconductor was about 1.125 times larger than that of the Y123 superconductor.
AtıfScopus12WoS9OpenAlex12İncele