- MakaleAçık Erişim2023Scopus SJRQ3High-cycle fatigue and tensile strength of AZ91 Mg alloy with MAO-epoxy duplex coating
Karabudak, Filiz
In this study, an epoxy layer was formed by the immersion process, on the oxide layer grown by the micro-arc oxidation (MAO) treatment of the AZ91 magnesium alloy, using the thin film sealing technology, and its effect on fatigue and tensile stress under high cycle conditions was investigated. The microstructures of the AZ91 base material, MAO/AZ91 and MAO-epoxy/AZ91 samples, which were subjected to high-cycle fatigue tests and uniaxial static tensile tests, were assessed through the scanning electron microscope (SEM), X-ray diffraction (XRD) mechanical tests, and fatigue and tensile tests. As a result, the MAO-epoxy duplex coating, which has a homogeneous and compact structure, was observed to improve the fatigue limit value/life, yield strength, ultimate tensile strength, and percentage elongation values of the base material significantly.
AtıfScopus2WoS2OpenAlex2İncele - MakaleYalnız künye2020Scopus SJRQ1Effects of Mn Content on Microstructure, Mechanical and Dry Sliding Wear Properties of Eutectic Al–Si–Cu Alloy
Alemdag, Yasin; Beder, Murat
Abstract: In the present study, effects of Mn content on microstructure, hardness, tensile and dry sliding wear properties of eutectic Al–Si–Cu alloy in as cast-state were investigated. Mn addition to the eutectic alloy results in the formation of α-Al15Mn3Si2 phase in its microstructure. It was found that hardness of eutectic alloy increases continuously with increasing Mn content while its tensile strength and percentage elongation values decrease. It was also found that the friction coefficient and volume loss of eutectic alloy decrease as Mn content increases. Amongst the alloys, the lowest friction coefficient is obtained with Al–12Si–3Cu–2Mn alloy yet the Al–12Si–3Cu–1Mn alloy exhibits the highest wear resistance. Formation of adhesion layer, its oxidation and delamination were observed to be main wear mechanisms of Al–12Si–3Cu–(0–2)Mn alloys. These findings are explained in terms of formation of α-Al15Mn3Si2 phase, and its cracking tendency effect. Graphic abstract: [Figure not available: see fulltext.].
AtıfScopus19WoS19OpenAlex19İncele