Sürdürülebilir Kalkınma Amaçları
Yazarlar
Yayınlar
- MakaleAçık Erişim2026Formulation of mechanical properties of hybrid fiber alkali-activated concretes by data analysis
Aksut, Yavuz Selim; Yetgín, Sukru
In this study, ground blast furnace slag (GBFS) and waste volcanic rock dust (RD) produced in a natural stone processing plant were used as binders. The binders were activated with Sodium Hydroxide (NaOH) and Sodium Silicate (Na2SiO3) to produce two types of concrete: alkali-activated concrete without fibers (AAC) and alkali-activated concrete with fibers (FAAC). In the production of concrete, steel and polyester fibers were used separately and hybrid at 0.25%, 0.50%, 0.75% and 1.0% by volume and a total of 117 15x15x15 cm cube specimens were produced. The mechanical properties of the specimens were evaluated by concrete surface hardness, ultrasonic pulse velocity and concrete compressive strength tests at 3, 7 and 28 days. The results obtained using non-destructive test methods were matched with concrete compressive strength values using various empirical formulas. Calculated concrete compressive strength values and actual concrete compressive strength values were compared using data analysis method. As a result, it was observed that there was a very significant correlation between the experimental compressive strength and the combined method in which 7-day surface hardness and ultrasound transmission rate were used together to calculate the compressive strength.
AtıfWoS1
İncele - MakaleYalnız künye2025Scopus SJRQ1Modeling the Compressive Strength of Fiber-Reinforced Alkali-Activated Concrete Using Non-Destructive Methods in Short Curing Periods
Aksüt, Yavuz Selim; Çullu, Mustafa; Yetgin, Sukru
The indirect assessment of concrete compressive strength using non-destructive techniques, including the Schmidt rebound hammer and ultrasonic pulse velocity methods, is crucial for evaluating and tracking the strength of structural concrete used in construction and rehabilitation projects. However, studies focusing on alkali-activated concrete (AAC) remain insufficient. This study investigates the mechanical properties of fiber-reinforced alkali-activated concretes (FAACs) produced with short curing times, addressing this gap in the literature. Ground blast furnace slag (GBFS) was used as the binder, and waste volcanic rock dust (RD), produced in a natural stone processing plant, served as a fine filler. These materials were activated with sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) to produce alkali-activated concrete, both without fibers (AAC) and with fibers (FAAC). Steel fiber (SF) and polyester fiber (PYF) were used separately and in hybrid forms at 0.25%; 0.50%; 0.75%, and 1.0% volume fractions, resulting in a total of 117 cubic specimens (15x15x15 cm). The specimens' mechanical properties were evaluated using regression analyses based on data from Schmidt rebound number (RN), ultrasonic pulse velocity (UPV) non-destructive methods and uniaxial compressive strength (UCS) destructive tests. Optimized functions predicting compressive strength based on RN and UPV measurements were developed, highlighting the significant effects of fiber type, ratio, and mode of use. Additionally, multivariate prediction models were statistically developed using data from the three test methods.
AtıfWoS2OpenAlex1İncele