- MakaleYalnız künye2016Scopus SJRQ1Investigation of structural and tribological properties of electroless Ni-B coated pure titanium
Çelik, Ilhan; Karakan, Mehmet; Bülbül, Ferhat
In the present study, the surface of commercial pure (Grade 2) titanium was coated with electroless Ni-B and, then, it was subjected to heat treatment for an hour at 400°. The surface morphology, microstructure and phase identification were analysed by X-ray diffraction and scanning electron microscope. Wear behaviour characterisation was carried out using a ball-on-disc tribometer. The results of the analyses showed that the electroless Ni-B coating had a significantly amorphous structure in the as-deposited condition. It was also determined that the coating structure crystallised after the heat treatment and wear resistance of pure titanium increased after electroless Ni-B coating. Particularly, upon the heat treatment, it was observed that wear resistance and surface hardness of pure titanium considerably increased.
AtıfScopus50WoS42OpenAlex41İncele - MakaleYalnız künye2014Scopus SJRQ2EFFECT OF HEAT TREATMENT ON STRUCTURE OF ELECTROLESS Ni-B COATED PURE TITANIUM
Bülbül, Ferhat; Çelik, Ilhan
Pure titanium has a very large potential for use industrially due to its low weight, however, its usage continues to be limited because it possesses some disadvantages such as low hardness and wear resistance, weak corrosion resistance in high temperatures and high cost. In order to strengthen these weaknesses of pure titanium, electroless Ni-B deposition process, may be an alternative solution. In this study, the Ni-B coatings were deposited on pure titanium and annealed at the temperatures of 450 degrees C, 650 degrees C and 850 degrees C. The non-heat treated and heat treated coatings were structurally characterized via SEM (scanning electron microscope) and XRD (x ray diffraction). These coatings transformed from amorphous structure to a pronounced crystalline structure depending on heat treatment.
AtıfWoS9TR Dizin2İncele