- MakaleAçık Erişim2025Scopus SJRQ1The effect of high B4C ratio on the improvement of mechanical properties and wear resistance of Al2024/B4C composites fabricated by mechanical milling-assisted hot pressing
Beder, Murat
In this study, the effects of 0 wt% (C0), 10 wt% (C1), 20 wt% (C2) and 40 wt% (C3) B4C content on the microstructure, mechanical properties and dry wear properties of Al2024/B4C composites were investigated. In order to prepare Al2024 matrix composites with different B4C particle contents, mechanical milling (MM) and hot pressing (HP) were employed as powder metallurgy methods. It was found that the θ (CuAl2) phase content in the microstructure of Al2024/B4C compact materials increased with increasing B4C particle reinforcement, reaching its highest value at 40 wt% B4C (C3) reinforcement ratio. As the B4C particle reinforcement content increased, the hardness values of the composite samples increased. Flexural strength values were 445.30 MPa, 495.20 MPa, 277.59 MPa, and 129.37 MPa for samples coded C0, C1, C2, and C3, respectively. It was found that the C0 sample without particle reinforcement exhibited more than 10 times the volume loss of the C3 sample with the highest particle reinforcement at 450 m sliding distance. The SEM examination of the friction surfaces of the Al2024/B4C composite samples showed that the worn surfaces were composed of delamination, adhesion and smearing layers.
AtıfScopus17WoS18OpenAlex18
İncele - MakaleAçık Erişim2025Scopus SJRQ2The effect of high SiC ratio on the physical, mechanical, tribological and corrosion behavior of Al2024 alloy matrix composites fabricated by powder metallurgy
Beder, Murat; Varol, Temel; Akçay, Serhatcan Berk; Çuvalcı, Hamdullah; Erdemir, Fatih; Khan, M Adam; Yıldız, Uğur Temel
Reinforcing materials used in the production of metal matrix composites are used to improve the properties of the final composite. However, the compatibility between matrix and reinforcement and the reinforcement ratio directly affects the properties of the composite material. For this reason, low reinforcement ratios are preferred in many studies on ceramic particle reinforced composites. Unlike conventional studies, in this study, the effects of 10 wt%, 20 wt% and 40 wt% SiC content on the microstructure, dry wear properties and corrosion properties of Al2024 matrix composites were investigated. θ phase content became higher as the SiC content was increased. Hardness values increased with increasing SiC reinforcement. The highest value (307.68 HB) was obtained for the composite with 40 wt% SiC reinforcement, an increase of more than 100%. A decrease in volume loss with increasing SiC reinforcement was observed in the friction and wear tests. For 5 N of load and 1200 m of sliding distance, it was found that an addition of 40 wt% of SiC particles in Al2024 matrix results decrease in volume loss by almost 722%.
AtıfScopus8WoS7OpenAlex7İncele - MakaleAçık Erişim2024Scopus SJRQ1Impact of high Al2O3 content on the microstructure, mechanical properties, and wear behavior Al–Cu–Mg/Al2O3 composites prepared by mechanical milling
Beder, Murat; Varol, Temel; Akçay, Serhatcan Berk
Metal matrix composites are increasingly being recognized as new wear-resistant materials. The main purpose of this study is to investigate the microstructure, mechanical properties, and wear resistance of Al–Cu–Mg alloy matrix composites reinforced with high contents of Al2O3 particles. Moreover, the effects of 10, 20, and 40 wt% Al2O3 contents on the microstructure, mechanical properties, and dry wear resistance of the Al–Cu–Mg matrix composites are studied. The results show that the θ (CuAl2) phase ratio increases with increasing Al2O3 contents. The hardness values of the samples also increase with increasing Al2O3 contents. The highest tensile and flexural strengths are measured as 284 and 562.9 MPa, respectively, and these values are obtained for the composite material reinforced with 10 wt% Al2O3 particles. The continuous increase in the hardness of the samples with increasing Al2O3 content may cause the lowest volume loss for the 40 wt% Al2O3-reinforced composite. The friction surfaces show that the wear surfaces comprise adhesion, delamination, and smear layers. Overall, compared to the Al2O3-reinforced composite samples, pure Al–Cu–Mg alloy samples show approximately 2 times more mass gain.
AtıfScopus20WoS17OpenAlex20İncele