- MakaleAçık Erişim2024Fatigue and tensile behaviour of Ti+TiN+Ti+TiVN multilayer nitride films coated on AZ91 magnesium alloy by closed field unbalanced magnetron sputtering
Alibeyoğlu, Fatih; Karabudak, Filiz; Yeşildal, Ruhi; Balcı, Arif; Efeoğlu, İhsan; Ateş, Onur Kazım
Despite their extensive use in the automotive and aerospace industries, Mg and Mg alloys, which are light metals, exhibit low fatigue and tensile strength. In this study, transition metal-nitride (TMN) multilayer coatings (Ti+TiN+Ti+TiVN) were coated twice on AZ91 Mg alloy using a Confined Field Unbalanced Magnetron Sputtering (CFUBMS) system to increase fatigue and tensile strength. The structural properties of the films were analyzed by using X-ray diffraction (XRD), scanning electron microscope (SEM), and energy dispersive spectrometry (EDS) methods, and the mechanical properties were analyzed by rotating bending fatigue and tensile testing machines. Ti+TiN+Ti+TiVN multilayer nitride surface coatings on AZ91 Mg alloys showed a dense and columnar microstructure and according to XRD results (111) was the preferred orientation with the dominant peak. The fatigue limit value of the AZ91 base material was fixed at 60.46 MPa, while it increased to 68.48 MPa after being coated with multilayer nitride. Along with the multilayer nitride coating, the tensile strength increased from 169.98 MPa to 175.43 MPa. As a result, the multilayer hard nitride coating with low surface roughness, which fills the defects, notches, and voids on the surface of the AZ91 base material, increased the fatigue and tensile strength in parallel. Based on the outcomes of the research, the literature has been enriched with an innovative approach through the enhancement of fatigue and tensile strengths by applying a CFUBMS coating to lightweight metals and alloys, such as AZ91, especially in the transportation industry where lightness and dynamic load resistance are essential.
- BildiriAçık Erişim2018Tribological Behaviour of Ti:Ta-DLC Films under Different Tribo-Test Conditions
Efeoglu, İhsan; Keleş, Ayşenur; Totik, Yaşar; Cicek, Hikmet; Süküroglu, Ebru Emine; Hamamci, M.; Gocer, A.; Karamis, M.B.; Nair, F.; Savas, S.
Diamond-like carbon (DLC) films are suitable applicants for cutting tools due to their high hardness, low friction coefficient and wear rate. Doping metals in DLC films have been improved its tribological properties. In this study, titanium and tantalum doped hydrogenated DLC films were deposited by closed-field unbalanced magnetron sputtering system onto M2 high speed steels in Ar/N2/C2H2 atmosphere. The friction and wear properties of Ti:Ta-DLC film were investigated under different tribo-test conditions including in atmospheric pressure, distilled water, commercial oil and Ar atmosphere. The coated specimens were characterized by SEM and X-ray diffraction techniques. The bonding state of C-C (sp3) and C=C (sp2) were obtained with XPS. The tribological properties of Ti:Ta-DLC were investigated with pin-on-disc wear test. Hardness measurements performed by micro-indentation. Our results suggest that Ti:Ta-doped DLC film shows very dense columnar microstructure, high hardness (38.2 GPa) with low CoF (μ ≈0.02) and high wear resistance (0.5E-6 mm3/Nm).