- MakaleAçık Erişim2026Scopus SJRQ2Experimental and Modeling Study of Fluidity in Ductile Iron (GGG40)
Coşar, Mehmet; Şüküroğlu, Ebru Emine; Güngör, Kadir; Çolak, Murat
Ductile irons (spheroidal graphite cast irons, SGI) are widely used in automotive and energy systems due to their high strength, ductility, and excellent machinability. The casting quality of these alloys largely depends on the flow and filling behavior of the molten metal, namely its fluidity. In this study, the effects of pouring temperature, filling time, and metallurgical quality on the fluidity of GGG40 ductile iron were investigated through both experimental and numerical approaches. Experimental trials were conducted at pouring temperatures of 1350 °C, 1400 °C, and 1450 °C; metallurgical quality levels of 10%, 50%, and 90%; and filling times of 5 s and 10 s. The fluidity lengths were measured and statistically evaluated. The results revealed that increasing the pouring temperature and metallurgical quality significantly improved fluidity, while shorter filling times allowed the molten metal to travel longer distances before solidification. Modeling studies performed using a commercial casting simulation software showed strong correlation with the experimental data. Microstructural examinations indicated that higher pouring temperatures and improved metallurgical quality led to a more homogeneous distribution of graphite nodules and an increased ferrite fraction in the matrix. The findings provide valuable insights into the influence of process parameters on the fluidity behavior of ductile iron and offer critical design data for enhancing casting quality and productivity in industrial foundry applications.
AtıfScopus1
İncele - MakaleAçık Erişim2025Scopus SJRQ2Investigation of the Effects of Filling Speed, Casting Temperature and Metallurgical Quality on Fluidity of Lamellar Graphite Cast Iron at Different Section Thicknesses
Köse, Sami; Çolak, Murat; Şüküroğlu, Ebru Emine
In this study, the fluidity properties of the alloy were investigated at different casting temperatures, different section thicknesses, and varying casting parameters of lamellar graphite cast iron materials. To achieve our goal, we utilized sand molds that were created with specific parameters including pouring temperature, metallurgical quality, section thickness, and fluidity test model. These molds were used for casting. Thus, the effect of fluidity properties in changing casting conditions and liquid metal advance distances at determined section thicknesses was investigated. Modeling was carried out with FlowCast casting simulation software by determining the liquid metal advance distance depending on the section thickness in the castings made in sand molds under changing casting conditions. The fluidity and advance distance of the liquid metal was determined comparatively with experimental and modeling techniques under the changing casting conditions in the parameters determined in this study. When the outcomes were examined; it was observed that different liquid metal advance distances occur at different cross-section thicknesses depending on the changing conditions.
AtıfScopus8WoS8OpenAlex7İncele - Yüksek Lisans TeziAçık Erişim2022Küresel grafitli dökme demir dökümünde dolum hızı, döküm sıcaklığı ve metalurji kalitesinin farklı kesit kalınlıkları üzerinde akıcılık özelliklerine etkisinin incelenmesi
Mehmet Coşar
Bu çalışmada, Küresel Grafitli Dökme Demir (KGDD) malzeme ile farklı döküm sıcaklıkları, kesit ölçüleri ve döküm uygulamalarında malzemenin akıcılık özelliklerinin incelenmesi amaçlanmıştır. Bu nedenle döküm sıcaklığı, metalürji kalitesi, çalışma ortamı için planlanan farklı kesit ölçülere göre akıcılık testi gerçekleştirilmiştir. Hazırlanmış kum kalıplara döküm işlemi yapılmış, akıcılık değerlerine etkileri ve değişen döküm işlemi koşullarında belirlenen kesit kalınlıklarında sıvı metal ilerleme ölçüleri incelenmiştir. Farklı döküm koşullarında kum kalıbı ile döküm işlemlerinde kesit ölçülerine göre ergimiş malzemenin kalıp içerisinde yürüme ölçüleri belirlenerek, FlowCast Döküm simülasyon yazılım programları ile değerlendirilmiştir. Bu nedenle çalışma kapsamında belirlenen malzemelerde değişen döküm şartlarında sıvı metalin akıcılığı ve ilerleme mesafeleri tespit edilmiştir. Bu çalışmada kum kalıba döküm, modelleme, deneysel tasarım, mikroyapı inceleme teknikleri kullanılmıştır.
- Yüksek Lisans TeziAçık Erişim2022Lamel grafitli (gri) dökme demirlerde dolum hızı, döküm sıcaklığı ve metalürji kalitesinin farklı kesit kalınlıklarında akıcılık özelliklerine etkisinin incelenmesi
Sami Köse
Bu çalışmada, lamel grafitli dökme demir malzemelerin farklı döküm sıcaklıkları, farklı kesit kalınlıkları ve değişen döküm parametrelerinde alaşımın akıcılık özellikleri araştırılmıştır. Bunun için döküm sıcaklığı, metalürji kalitesi, farklı malzemeler, özel olarak tasarlanmış kesit kalınlıkları bulunan akıcılık testi modeli ile hazırlanmış kum kalıplarına dökümü gerçekleştirilmiştir. Böylece değişen döküm koşullarında akıcılık özelliklerinin etkisi ve belirlenen kesit kalınlıklarında sıvı metal ilerleme mesafeleri incelenmiştir. Değişen döküm koşullarında kum kalıbında yapılmış dökümlerde kesit kalınlıklarına bağlı sıvı metal ilerleme mesafesi belirlenerek, FlowCast Döküm simülasyon yazılımları ile modellemeler gerçekleştirilmiştir. Böylece çalışma kapsamında belirlenen parametrelerde değişen döküm şartlarında sıvı metalin akıcılığı ve ilerleme mesafesi deneysel ve modelleme teknikleri ile karşılaştırmalı olarak tespit edilmiştir.