- MakaleYalnız künye2025Scopus SJRQ2Investigation of structural and adhesion properties of ZnO and h-BN doped TiO2 coatings on Cp–Ti alloy
Belet, Ali Kadir; Şüküroğlu, Süleyman; Şüküroğlu, Ebru Emine
Titanium and its alloys are widely used in aircraft, automotive, chemistry, marine, and military industries owing to their superior properties such as specific strength, very low density, high melting point, high corrosion resistance, good fatigue strength and toughness, low elastic modules, and excellent biocompatibility. However, insufficient tribological properties such as high and unstable friction coefficient, low scraping wear resistance and strong adhesion tendency, and poor corrosion resistance in some aggressive corrosive environments such as severe chloride solution limits the use of titanium and its alloys in some engineering applications. For this reason, it has become quite common to change and/or improve the surface properties of titanium and its alloys. In this study, the structural properties of TiO2 coatings with zinc oxide (ZnO) added TiO2 and hexagonal boron nitride (h-BN) added TiO2 grown composite coatings, respectively, on Cp–Ti substrates by micro-arc oxidation method and the adhesion behavior between the base material and coatings were investigated.
AtıfScopus1WoS1OpenAlex1
İncele - MakaleAçık Erişim2024Scopus SJRQ4Investigation of friction behavior of TiO2: Al2O3 composite coating formed on AA2024 alloy by micro-arc oxidation
Boynueğri̇ Kaplan, Emine; Şüküroğlu, Ebru Emine
In this study, an alumina (Al2O3) ceramic coating and a composite coating containing titanium dioxide (TiO2) particles were prepared on surfaces of AA2024 substrates by micro-arc oxidation (MAO) treatment. The effects of micro-sized (≈20-30 µm) TiO2 particles incorporated into electrolyte on the microstructure, phase and chemical composition, thickness, and friction behavior of the coating were investigated. The surface morphologies of the coatings were analyzed by scanning electron microscopy (SEM). The phase and chemical compositions of the coatings were evaluated by means of X-ray diffraction (XRD) and energy-dispersive X-ray spectrometry (EDS), respectively. The friction coefficient of the coatings was investigated using a pin-on-disc tribometer under condition of dry slip sliding. Moreover, the wear tracks were analyzed by SEM. Addition of TiO2 particles into the electrolyte resulted in the reduction in number of pores and formation of smaller and more uniform pores in comparison with the Al2O3 ceramic coating. XRD analyses demonstrated that the TiO2:Al2O3 composite coating was composed of anatase-TiO2 and rutile-TiO2, as well as pure aluminum, α-Al2O3 and γ-Al2O3 which are the primary phases. The friction tests showed a significant reduction in the friction coefficient of the composite coated samples which contains titanium oxide (TiO2) particles in comparison with Al2O3 coated and uncoated samples. Copyright 2021, Yıldız Technical University.
AtıfScopus1WoS1İncele