- MakaleAçık Erişim2025Scopus SJRQ2Investigation of Tensile and Fatigue Behavior of Cr/CrN/TiCrN/TiCrCN Multilayer Films Coated on AA6063 and AZ91 Alloys by Closed-Field Unbalanced Magnetron Sputtering Process
Yeşildal, Ruhi; Sezer, Sadberk; Karabudak, Filiz
Despite the widespread use of Mg and Al alloys among light metals in the automobile and aviation industries, they have low tensile and fatigue strength. Therefore, in the present work, AZ91 Mg and AA6063 Al alloys were coated with a multilayer transition metal nitride film (Cr/CrN/TiCrN/TiCrCN) to increase fatigue and tensile strength. Films with Cr/CrN/TiCrN/TiCrCN microstructure architecture were synthesized on the surfaces of AZ91 Mg and AA6063 Al alloys using the CFUBMS (closed-field unbalanced magnetron sputtering) system, one of the PVD (physical vapor deposition) techniques. Films’ structural properties were analyzed by XRD, SEM, and EDAX, whereas mechanical properties were investigated using tensile and rotary bending fatigue testing machines. According to the SEM examination, the Cr, CrN, TiCrN, and TiCrCN multilayer nitride films on the two alloys have a columnar and dense microstructure. The XRD analysis detected Cr (211), CrN (111) and (200), TiN (111), (200) and (222), and TiCN (200) and (311) diffraction peaks. The Cr/CrN/TiCrN/TiCrCN multilayer coating increased the fatigue limit value of AZ91 by 11.22% from 70.26 MPa to 78.15 MPa. The fatigue limit value of AA6063 decreased by 9.79% from 79.71 MPa to 71.9 MPa. After coating, the tensile strength value of AZ91 increased from 137.89 MPa to 139.65 MPa, while the tensile strength of AA6063 decreased from 129.35 MPa to 118.16 MPa.
AtıfScopus2WoS2OpenAlex2İncele - MakaleYalnız künye2018Scopus SJRQ2Investigation of high temperature wear resistance of TiCrAlCN/TiAlN multilayer coatings over M2 steel
Sukuroglu, E.E.; Baran, O.; Totik, Y.; Efeoglu, I.
In this study, TiCrAlCN/TiAlN multilayer coatings were deposited on M2 high speed steel substrates by the Closed-Field Unbalanced Magnetron Sputtering system. The chemical composition, microstructure, morphology, mechanical and high temperature wear resistance properties of the coatings were characterized, analyzed and compared to the substrate. The high temperature wear tests were carried out under a load of 2 N at the lap (wear test distance) of 50 m and in dry sliding condition at Room Temperature (RT), 150, 300, 450, and 600 °C on atmospheric conditions. It has been found that the TiCrAlCN/TiAlN multilayer coatings have a higher wear resistance than the M2 substrate. The stable friction behavior and low friction tendency was determined at 600 °C. When the test temperature increased, the wear rates decreased. Narrow and smooth wear tracks and also the lowest wear rate were obtained at 600 °C.
AtıfScopus6WoS6OpenAlex8İncele - MakaleYalnız künye2016Scopus SJRQ2The investigation of adhesion and fatigue properties of TiN/TaN multilayer coatings
Baran, Ö.; Sukuroglu, E.E.; Efeoglu, İ.; Totik, Y.
TiN/TaN multilayer coatings exhibit excellent mechanical properties when compared to single layer nitride coatings. In this study, TiN/TaN multilayer coatings were deposited on Mo-alloy and W-alloy substrates by CFUBMS. The structural and mechanical properties of coatings were analysed using XRD, EDS, SEM and a micro-hardness tester, respectively. To determine the adhesion and fatigue behaviour of the coatings were performed a scratch test in two modes that a standard mode with progressive loading and sliding-fatigue multimode operation with unidirectional sliding, respectively. A microscope was used to characterize adhesion and fatigue failures. The structural, mechanical, adhesion and fatigue properties of TiN/TaN multilayer coatings significantly changed depending on the substrate.
AtıfScopus14WoS12OpenAlex13İncele