Sürdürülebilir Kalkınma Amaçları
Yayınlar
- MakaleAçık Erişim2024Deep eutectic solvent as plasticizing agent for the zein based films
Yilmaz, Mustafa Tahsin; Kul, Ebubekir; Saricaoglu, Furkan Turker; Odabas, Halil Ibrahim; Taylan, Osman; Dertli, Enes
This study explores, the impacts of incorporating of deep eutectic solvent (DES) as plasticizer on the characteristics of zein films. Investigation focused on examining the mechanical, thermal, surface, and microstructural properties of zein films that were plasticized using DES. The findings of the study revealed that by adding DES to zein films, there was an observed improvement in transparency. Additionally, it was observed that up to a 20% addition of DES led to a reduction in water vapor permeability (WVP). However, beyond this level, the WVP increased as the surface hydrophobicity decreased. The films that were plasticized with DES showed higher tensile and burst strength values than control. However, there was a decrease in the elongation at break and burst distance, except for the film containing 30% DES. The addition of DES as plasticizer resulted in smoother surface morphology compared to the control, and all films revealed homogeneous and non-porous surface and cross-section microstructure. The films plasticized with DES displayed three different thermal degradation temperatures resulting in higher thermal stability. The FT-IR spectrum of films showed similar backbone structure including Amide I, II and III bands. However, 5% DES plasticized film showed different secondary structural peaks of Amide I band due to lower α-helix and higher β-sheet and random coil content. The findings of this investigation indicate that the employment of DES as plasticizer in biodegradable polymer films can yield enhanced mechanical and barrier characteristics compared to conventional plasticizers, thus demonstrating its potential for effective use.
- MakaleYayıncıda açık erişim2024Gelatin extraction from chicken skin by conventional and Ohmic heating methods and comparison with commercial halal gelatins
Işık, Çiğdem; Parlak, Mahmut Ekrem; Kıraç Demirel, Fatma Tuba; Odabaş, Halil İbrahim; Dağdelen, Adnan Fatih; Yilmaz, Mustafa Tahsin; Taylan, Osman; Sarıcaoğlu, Furkan Türker
Gelatin extraction from chicken skins using ohmic heating (OH) is a promising application in the food industry. In this study, the effects of OH parameters (electric field (5, 10, 15, and 20 V/cm) and extraction time (1, 3, and 5 h)) on the extraction yield, physicochemical, functional, rheological, thermal, and microstructural properties of chicken skin gelatin were investigated, as well as comparison with conventional extraction and commercial halal gelatins. Chicken skin gelatins obtained with OH-assisted extraction showed higher ash content resulting in more turbidity than commercial gelatins. OH parameters significantly increased the gelatin yield, and 1 h of OH treatment revealed the highest gel strength amongst the electric field applications, conventional extracted, and bovine gelatin. The melting and gelation temperatures of chicken skin gelatins were higher than bovine gelatin and OH treatment increased the thermal stability. The amino acid composition significantly changed with OH treatment, and total imino acid content, relating to the gelation properties, increased. Functional properties, water and oil binding, emulsifying, and foaming, of chicken skin gelatin were significantly higher than commercial gelatins, and OH treatment significantly increased these properties. Overall, OH extraction of gelatin from chicken skins could be a better option for less extraction time, higher extraction yield, better functionality, and higher thermal stability compared to conventional extraction. It was concluded that chicken skin gelatins extracted using OH have properties that can be an alternative to commercial gelatins, but further purification processes are required.