Kumaş, Cavit; Ergül, Burcu; Sayin, Zehra Ebru

Activated carbon was prepared from hazelnut shell by chemical activation. In practice, activation was provided  K2CO3  and  K2CO3  +  H3BO3  treatment  with  hazelnut  shell.  In  order  to  find  the  optimum activated carbon, different K2CO3 (15 %, 30 % and 45 %) and H3BO3 (3%, 5% and 10%) concentration, activation  temperature  (500,  600,  750,  900°C)  and  carbonization  time  (30,  60  and  120  minute)  was employed. The produced activated carbon samples, moisture content, ash content, carbonization yield, iodine  number,  hardness,  surface  area,  mercury  porosimetry,  SEM  and  adsorption  capacity  were studied  to  determine  the  optimum  sample.  As  a  result  of  studies,  optimum  activated  carbon  was obtained  at  5%  boric  acid  and  30  %  potassium  carbonate  acid  concentration,  900°C  carbonization temperature  and  60  minute  carbonization  time.  The  obtained  iodine  number  of  activated  carbon 1009.71  mg/I2,  surface  area  780.31  m2/g  was  determined.  Also  made  hardness  and  adsorption  tests produced results of high hardness of the active carbon (93.33 %) and was found to have high adsorption capacity.  Due  to  having  low  moisture  and  ash  content  with  high  surface  area,  hardness,  of  hazelnut shell is considered to be a potential raw material for producing activated carbon.