- MakaleAçık Erişim2026Process Optimization of Spray-Dried Aquafaba and Comparison with Freeze-Drying: Techno-Functional Performance and Structural Attributes
Tunc Odabas, Merve Tugce; Saricaoglu, Furkan Turker; Parlak, Mahmut Ekrem; Akdogan, Arda; Odabas, Halil Ibrahim; Gündogdu, Engin; Simsek, Senay; Atalar, Ilyas
This study aimed to optimize the spray-drying (SD) process for aquafaba and compare the physical and techno-functional properties of the resulting powder with those of its freeze-dried (FD) counterpart. A Box-Behnken design was employed to evaluate the effects of inlet air temperature (150-190 degrees C), air speed (3.5-4.3 m/s), and feed flow rate (0.3-0.5 L/h) on 14 quality responses. The optimized SD conditions were determined to be an inlet air temperature of 189 degrees C, an air speed of 4.2 m/s, and a feed flow rate of 0.3 L/h. Validation experiments demonstrated that the developed models had high predictive capacity, with only a small discrepancy (0.56-5.88%) between the predicted and experimental values. Comparative analysis showed that the optimized SD powder had significantly lower moisture content (2.47%) and water activity (0.18) than the FD powder (3.51% and 0.34, respectively), indicating superior storage stability. In addition, the SD powder exhibited greater whiteness (82.37), higher water solubility (88.44%), and substantially greater foaming capacity (266.67%) than the FD sample (243.33%). Although the FD powder demonstrated better wettability and water absorption capacity because of its porous structure, FTIR spectroscopy and protein secondary structure analysis confirmed that SD preserved the functional integrity of aquafaba. Specifically, SD induced a transition from disordered random-coil structures to more ordered beta-sheet and beta-turn configurations, thereby improving foaming performance. Overall, these findings indicate that optimized spray-drying is a highly efficient and industrially scalable alternative to freeze-drying for producing functional aquafaba powder for use as a plant-based egg substitute.
- MakaleAçık Erişim2024Deep eutectic solvent as plasticizing agent for the zein based films
Yilmaz, Mustafa Tahsin; Kul, Ebubekir; Saricaoglu, Furkan Turker; Odabas, Halil Ibrahim; Taylan, Osman; Dertli, Enes
This study explores, the impacts of incorporating of deep eutectic solvent (DES) as plasticizer on the characteristics of zein films. Investigation focused on examining the mechanical, thermal, surface, and microstructural properties of zein films that were plasticized using DES. The findings of the study revealed that by adding DES to zein films, there was an observed improvement in transparency. Additionally, it was observed that up to a 20% addition of DES led to a reduction in water vapor permeability (WVP). However, beyond this level, the WVP increased as the surface hydrophobicity decreased. The films that were plasticized with DES showed higher tensile and burst strength values than control. However, there was a decrease in the elongation at break and burst distance, except for the film containing 30% DES. The addition of DES as plasticizer resulted in smoother surface morphology compared to the control, and all films revealed homogeneous and non-porous surface and cross-section microstructure. The films plasticized with DES displayed three different thermal degradation temperatures resulting in higher thermal stability. The FT-IR spectrum of films showed similar backbone structure including Amide I, II and III bands. However, 5% DES plasticized film showed different secondary structural peaks of Amide I band due to lower α-helix and higher β-sheet and random coil content. The findings of this investigation indicate that the employment of DES as plasticizer in biodegradable polymer films can yield enhanced mechanical and barrier characteristics compared to conventional plasticizers, thus demonstrating its potential for effective use.
- MakaleAçık Erişim2024Characterization of biodegradable bi-layer films from thermoplastic starch and poly-l-lactic acid
Parlak, Mahmut Ekrem; Uzuner, Kubra; Ozdemir, Sebahat; Kirac Demirel, Fatma Tuba; Dundar, Ayse Neslihan; Sahin, Oya Irmak; Dagdelen, Adnan Fatih; Odabas, Halil Ibrahim; Saricaoglu, Furkan Turker
This study aimed to enhance the oxygen barrier properties of polylactic acid (PLA) film, a biodegradable packaging material with high oxygen permeability (OP). Bi-layer films were produced by coating thermoplastic starch (TPS) onto PLA films in various ratios while maintaining constant film thickness. The mechanical, optical, barrier, thermal, hydrophobicity, moisture sorption, and microstructural properties of the films were analyzed. Increasing the TPS ratio elevated moisture content (MC), water uptake, solubility, and opacity while enhancing UV barrier properties. TPS coating reduced tensile and burst strength but increased the burst deformation of the bi-layer films. Bi-layer film production resulted in a water vapor permeability increase of 59.26%–94.44% compared with neat PLA while decreasing OP by 2.52%–29.66%. The equilibrium moisture content (EMC) rose with higher TPS ratios, displaying type II isotherms. FTIR analysis indicated no chemical interactions between PLA and TPS. Increasing the TPS ratio decreased PLA crystallinity, supporting the mechanical and barrier properties of the bi-layer films. Neat and bi-layer films exhibited smooth, homogeneous surfaces, with a visible interface in the cross-section of the bi-layer films. In conclusion, TPS shows promise as an alternative to improve oxygen barrier properties in PLA films without adversely affecting other properties.
- MakaleYalnız künye2020Process for production of microencapsulated anthocyanin pigments from Rosa pimpinellifolia L. fruits: optimization of aqueous two-phase extraction, microencapsulation by spray and freeze-drying, and storage stability evaluation
Odabas, Halil Ibrahim; Koca, Ilkay
Rosa pimpinellifolia L. fruits (RPF) are promising source of anthocyanin pigments. The objectives of this study were to optimization of the aqueous two-phase extraction (ATPE) process of anthocyanin from RPF and microencapsulation of anthocyanin-rich RPF extract. The optimal ATPE conditions were as follows: 0% HCl, 30% ethanol, 19% ammonium sulfate, and liquid to solid ratio 51.71, 97.71 min, and 30 degrees C extraction temperature. Predicted anthocyanin yield at the optimum conditions was 1578.90 mg cyanidin 3-glucoside equivalent/100 g dry fruit. ATPE resulting in 1.80-fold increase in the purity of anthocyanins when compared to conventional solvent extraction (CSE). The composition of the anthocyanins were determined with HPLC-QTOF-MS. Freeze-drying and spray-drying methods were employed for the production of microencapsulated anthocyanin pigments. The half times of microencapsulated anthocyanins at 4, 25 and 37 degrees C were determined as 12.16, 6.60 and 3.12months for freeze-dried microcapsules, and 16.50, 9.24 and 4.29 months for spray-driedmicrocapsules, respectively.