  Strength and ultrasonic properties of cemented paste backfill

  Ercikdi, Bayram; Yilmaz, Tekin; Külekci, Gökhan

  This paper presents the strength (UCS) and ultrasonic pulse velocity (UPV) properties of cemented paste backfill (CPB) produced from two different mill tailings (Tailings T1 and T2). A total of 240 CPB samples with diameter × height of 5 × 10 cm and 10 × 20 cm prepared at different binder dosages (5-7 wt.%) and water-to-cement ratios (3.97-5.10) were subjected to the UPV and UCS tests at 7, 14, 28 and 56-days of curing periods. UCS and UPV of CPB samples increased with increasing the binder dosage and reducing the w/c ratio irrespective of the sample size and tailings type. CPB samples with a diameter × height of 5 × 10 cm were observed to produce consistently higher (up to 1.69-fold) UCSs than those of 10 × 20 cm CPB samples at all binder dosages and w/c ratios. However, at the corresponding binder dosages and w/c ratios, the maximum variation of UPV between the CPB samples of 5 × 10 cm and 10 × 20 cm was only 7.45%. Using the method of least squares regression, the UCS values were correlated with the UPV values for CPB samples of 10 × 20 cm in size. A linear relation with a high correlation coefficient appeared to exist between the UCS and UPV for CPB samples. These findings suggest that the UPV is essentially independent of the sample size. In this regard, the UPV test can be suitably exploited for the rapid estimation of the strength and quality of CPB samples even using small samples with concomitant benefits of reducing sample size.

  • 
  AtıfScopus126·WoS108·OpenAlex125

  İncele
• MakaleYalnız künye2014Scopus SJRQ1/r/gumushane/15723
  Assessment of strength properties of cemented paste backfill by ultrasonic pulse velocity test

  Yilmaz, Tekin; Ercikdi, Bayram; Karaman, Kadir; Külekçi, Gökhan

  Ultrasonic pulse velocity (UPV) test is one of the most popular non-destructive techniques used in the assessment of the mechanical properties of concrete or rock materials. In this study, the effects of binder type/dosage, water to cement ratio (w/c) and fines content (<20 μm) of the tailings on ultrasonic pulse velocity (UPV) of cemented paste backfill (CPB) samples were investigated and correlated with the corresponding unconfined compressive strength (UCS) data. A total of 96 CPB samples prepared at different mixture properties were subjected to the UPV and UCS tests at 7, 14, 28 and 56-days of curing periods. UPV and UCS of CPB samples of ordinary Portland cement (CEM I 42.5 R) and sulphate resistant cement (SRC 32.5) initially increased rapidly, but, slowed down after 14 days. However, UPV and UCS of CPB samples of the blast furnace slag cement (CEM III/A 42.5 N) steadily increased between 7 and 56 days. Increasing binder dosage or reducing w/c ratio and fines content (<20 μm) increased the UCS and UPV of CPB samples. UPV was found to be particularly sensitive to fines content. UCS data were correlated with the corresponding UPV data. A linear relation appeared to exist between the UCS and UPV of CPB samples. These findings have demonstrated that the UPV test can be reliably used for the estimation of the strength of CPB samples.

  • 
  AtıfScopus145·WoS133·OpenAlex136