Sukuroglu, Ebru Emine; Sukuroglu, Suleyman; Akar, Kubra; Totik, Yasar; Efeoglu, Ihsan; Arslan, Ersin

NiTi alloys exhibit good properties, such as shape memory behavior, high corrosion resistant, having the closest elasticity modulus of a human bone and superior biocompatibility properties. However, the surface problems that arise during the use of this alloy limit the usage in the industry and health sector. In recent years, micro-arc oxidation method is used to improve the surface properties and increase the usage of these alloys. In this study, the TiO2 coatings were deposited on the NiTi substrates. The surface topography, morphology, crystallographic structure, and thickness of the coatings were determined using scanning electron microscopy and X-ray diffraction. The corrosion properties were investigated using potentiostat test unit in two different media such as NaCl solution and simulated body fluid. The results show that the coated samples have higher corrosion resistance than uncoated samples in the two different media.

Çelik, Ilhan; Karakan, Mehmet

In this study, plasma nitriding treatment was applied to commercially pure titanium (Grade 2). Structural properties, electrochemical and tribological behaviours of the nitrided pure titanium specimens were comparatively investigated. Microstructure and morphology of the plasma nitrided specimens were analysed by X-ray diffraction and scanning electron microscopy. Furthermore, corrosion tests were conducted in Ringer's solution, which represents a human body environment, to determine electrochemical properties. Then, tribological and frictional properties were investigated using pin-on-disc tribometer, and a micro-hardness tester was used to measure the hardness of the coatings. The results showed that plasma nitrided specimens exhibited higher surface hardness than the untreated specimens did. In addition, the plasma nitrided specimens at 700 °C presented significantly better performance than the other plasma nitrided specimens (at 500 °C and 600 °C) under dry wear conditions. Moreover, corrosion test results showed that corrosion behaviours of untreated and nitrided samples had similar characteristic.