  Daulay, Amru; Yassaroh, Yassaroh; Samada, Lukmanul Hakim; Amrulloh, M. Hanif; Kumaş, Cavit; Nariswari, Mentari Kirana; Putri, Devi Mariska; Chambioso, Yugo

  Alternative binders that can be processed in water are still in the early stages of development for more efficient and sustainable supercapacitors. However, their electrochemical performance is still below average. This study uses heat-moisture-treated starch (starch HMT) as a binder for reduced graphene oxide (rGO) supercapacitors. Starch HMT has been fabricated at 120 °C. The XRD diffractogram exhibits peaks at 2θ angles of 15°, 17°, 22°, and 24°. The 2θ values indicate that potato starch is of type B. FTIR spectra show the formation of OH, C–O–C, C-O, C–O–C, and C-H bonds. SEM images show cracks in the morphology. Electrochemical testing shows a specific capacity of 230 F/g at a current density of 1 A/g. The charge–discharge stability of the electrodes at 5000 cycles is 90%. These results offer a framework for developing electrode materials and binders for supercapacitors.

  • 
  • 
  • 
  İncele
• MakaleYalnız künye2023/r/gumushane/12586
  The effect of fabrication method on physical properties of different Y211 and 20% Ag2O added YBCO sample

  Duman, Şeyda; Çakır, Bakiye; Başoğlu, Mehmet; Küçükömeroğlu, Tayfur; Aydıner, Alev

  In this study, it is aimed to investigate the effects of production methods on the physical properties of 20% Ag2O and different ratios of Y211 added YBCO samples. In this context, the samples with Y123 + x % (x = 20, 25, 30) Y211 + 20%Ag2O compositions were fabricated by MPMG and TSMG methods in two groups to join YBCO main samples. XRD measurements were performed to determine the characteristic peaks. Trapped magnetic fields and vertical levitation forces between the bulk samples and a permanent magnet were measured using a computer-controlled system in ZFC at 77 K. From the XRD measurements, it was found that MPMG YBCO samples had a dominant superconducting structure and partially showed orientation peaks in the c-axis direction, while TSMG YBCO samples were single-crystal samples oriented along the c-axis. From the trapped magnetic field measurement results, the trapped magnetic field value of the Y123 + 25%Y211 + 20%Ag2O (TAg25) sample prepared by the TSMG method was higher than that of the other samples. Among the levitation force measurement results, the maximum repulsive force values of TAg25 and TAg30 (Y123 + 30%Y211 + 20%Ag2O) samples are the highest. At the same time, the hysteresis widths of these samples are also the highest, which proves that their flux-pinning potential is higher than that of the other samples.