  Optimization of rare earth elements recovery from Kızıldag (Karaman-Türkiye) shale ore using response surface methodology

  Uysal, Turan; Ünal, Ceren Erust; Akça, Muhammet Esat; Sis, Hikmet; Erdemoğlu, Murat

  In this study, the usability of bauxite-related shale ore, rich in Rare Earth Elements (REEs), to produce REEs, which have high added value and critical importance, was investigated. In this context, Kızıldag (Karaman-Türkiye) shale ore, was prepared for tests through size reduction and sampling processes. HCl leaching was performed at different acid concentrations, leaching times, leaching temperatures, and liquid/solid ratios to determine the optimum leaching conditions for the milled ore. The modeling and optimization parameters related to leaching recovery were investigated using the response surface method (RSM). The results were evaluated using analysis of variance, three-dimensional graphs were drawn, and the accuracy of the models was discussed. Accordingly, optimum values were found, and the REE leaching recovery corresponding to these optimum values was 49.13%. It was concluded that the optimization results were compatible with the experimental results, and the average error rate (6.35%) was low.

  • 
  İncele
• MakaleAçık Erişim2021/r/gumushane/14843
  Effect of heating on structure and leaching characteristics of a zinc carbonate ore

  Kumas, Cavit; Obut, Abdullah

  In this work, the structural changes occurred in a zinc carbonate (smithsonite) ore sample following heating at temperatures between 523 K and 1173 K were investigated in detail using X-ray diffraction (XRD), thermal (TG/DTA) and Fourier-transform infrared (FT-IR) spectroscopy analyses. Afterwards, the leaching characteristics of zinc from the ore sample and the heated ore samples in sodium hydroxide solutions were determined. While heating at 523 K did not cause any structural change in the ore sample, heating at 723 K completely converted smithsonite (ZnCO3) in the ore sample to zinc oxide (ZnO), which resulted lower zinc leaching efficiencies of 40.6% and 62.0% for 3 and 4 mol/dm3 NaOH concentrations, respectively, in comparison to zinc leaching efficiencies (67.2% and 70.7%) obtained for the unheated ore sample. On the other hand, due to neoformation of dissolution resistant ZnFe2O4, Ca2ZnSi2O7 and ZmSiO4 phases during heating and formation of CaZm(OHD2H2O phase during leaching, the leaching efficiency of zinc further decreased to 22.2% and 31.3%, respectively, in 3 and 4 mol/dm3 NaOH solutions for the ore sample heated at 1173 K. The formation of zinc-containing dissolution resistant phases by high-temperature heating was observed to be the only reason for the reduction in the zinc leaching efficiency (49.4% at 1173 K) at the highest NaOH concentration (8 mol/dm3) studied. In this work, the comparative precipitation studies were also conducted and crystalline zinc oxides with different morphologies could be precipitated at considerably high efficiencies from the selected pregnant solutions obtained following leaching.