2026-10-23T17:04:06Zhttps://gumushane-rdlopen.rawdatalibrary.net/oai/requestoai:gumushane-rdlopen.rawdatalibrary.net:gumushane/119422026-10-22T11:27:41Zopenairedrivercom_gumushane_10000col_gumushane_10001com_gumushane_10007col_gumushane_10171Effect of aging time and temperature on properties of AA7075 alloy; [Yaşlandırma süresinin ve sıcaklığının AA7075 alaşımının özelliklerine etkisi]Budak, SelahattinÇolak, HarunYakut, YusufAgingCompressive strengthHardnessIn this study, the effect of aging at different temperatures and times on the properties of AA7075-T6 alloy was investigated. The samples prepared for the experimental studies were subjected to the solution, quenching, and then aging heat treatment at 100 °C and 200 °C for different periods (42-66-90 hours). The properties of the experimental samples were investigated by hardness, compression test, and scanning electron microscope (SEM). As a result of the studies, it was determined that the aging heat treatment had a positive effect on the microstructure and mechanical properties of the AA7075 alloy compared to the reference sample. Especially as a result of the heat treatments at 100 °C, higher results were obtained in hardness and compression strength compared to the initial values.Gumushane University2023Articlehttps://rdlopen.rawdatalibrary.net/r/gumushane/11942https://doi.org/10.17714/gumusfenbil.10998822146-538XenGumushane Universitesi Fen Bilimleri Dergisiinfo:eu-repo/semantics/openAccessinfo:eu-repo/semantics/articlehttps://gumushane-rdlopen.rawdatalibrary.net/tr/items/gumushane/11942